Standard PM Fiber
Fibercore’sPolarization Maintaining (PM) fibers are designed to give the highest levels ofpolarization maintenance for wavelengths from 488nm to greater than 1550nm.These fibers can be used in interferometric sensors, modulators, delay lines,spectroscopy and biomedical applications.
Fibercore use ‘Bow-Tie’ Stress Applying Parts (SAPs) to create birefringence inthe core. The design of these highly efficient SAPs generate very highbirefringence without excessive stress, allowing polarization orientation to becontrolled effectively across a fiber system.
‘BowTie’ PM Fiber
Thecore is flanked by areas of high expansion, boron-doped glass, which shrinkback more than the surrounding silica. Tension caused induces birefringence(creating two different indices of refraction: a higher index parallel and alower index perpendicular to the applied stress).
Fibercore’s ‘Bow-Tie’ design is capable of creating more birefringence than anyother stressed design. This is simply because it is based on two opposingwedges, the most simple and efficient means of applying stress to a point.
Advantages:
• Highly birefringent
• Short beat-length
• Strong Polarization Extinction Ratio (PER) maintaining
• Broad wavelength ranges
Typicalapplications:
• Interferometric sensors
•Diode pigtails
• Coherent beam delivery
•Modulators
• Delay lines
• Spectroscopy
•Biomedical
ProductVariants:
• HB450 PM Fiber for wavelengths above 450nm
• HB600 PM Fiber for wavelengths above 600nm
• HB750 PM Fiber for wavelengths above 750nm
• HB800 PM Fiber for wavelengths above 800nm
• HB1000 PM Fiber for wavelengths above 1020nm
• HB1250 PM Fiber for wavelengths above 1270nm
• HB1500 PM Fiber for wavelengths above 1520nm
Specifications
| HB450 | HB600 | HB750 | HB800 | HB1000 | HB1250 | HB1500 |
Operating Wavelength (nm) | 488 - 633 | 633 - 780 | 780 - 830 | 830 - 1060 | 1060 - 1300 | 1300 - 1550 | 1550 - 1650 |
Cut-Off Wavelength (nm) | 350 - 470 | 500 - 600 | 610 - 750 | 600 - 800 | 840 -1020 | 1030 -1270 | 1230 -1520 |
Numerical Aperture | 0.10 - 0.13 | 0.14 - 0.18 |
Mode Field Diameter (μm) | 3.0 – 4.1 @488nm | 2.8 – 3.7 @633nm | 3.5 – 4.6 @780nm | 3.7 – 4.9 @830nm | 4.7 – 6.3 @1060nm | 5.8 – 7.9 @1310nm | 7.0 – 9.2 @1550nm |
Attenuation (dB/km) | ≤100 @488nm | ≤15 @633nm | ≤8 @780nm | ≤5 @830nm | ≤3 @1060nm | ≤2 @1310nm | ≤2 @1550nm |
Beat Length (mm) @633 | <2.0 |
Proof Test (%) | 1 (100 kpsi) |
Cladding Diameter (μm) | 125 ± 1 |
Core Cladding Concentricity (μm) | ≤0.75 | ≤1.0 |
Coating Diameter | 245 ± 15 |
Coating Type | Dual Acrylate |